Titanium trichloride catalyst component and the process for the production thereof

ABSTRACT

A titanium trichloride catalyst component containing a minor amount of prepolymerized alpha-olefin and useful in the polymerization of alpha-olefins is produced by reducing titanium tetrachloride with an organoaluminum compound at low temperatures and then treating the resulting reduced solids product with about 1 to 1,000 wt. % alpha-olefin so as to obtain a prepolymerized titanium trichloride reduced solid. The prepolymerized reduced solid can thereafter be activate to a highly active prepolymerized titanium trichloride by treating the prepolymerized reduced solid with a halogenated hydrocarbon and a Lewis base complexing agent or titanium tetrachloride and a Lewis base complexing agent. The prepolymerized reduced solid and the prepolymerized activated titanium trichloride manifests substantially no evidence of friability upon being subjected to mechanical shearing forces. The resulting prepolymerized activated titanium trichloride composition, when employed in combination with an organo-metal compound results in an unexpectedly highly active catalyst obtaining polymers with high heptane insolubles.

This is a continuation of application Ser. No. 102,677, filed Dec. 12, 1979, now abandoned, which is a division of application Ser. No. 945,929, filed Sept. 26, 1978, and now U.S. Pat. No. 4,295,991, issued Oct. 20, 1981.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a titanium trichloride useful as a Ziegler-type catalyst component. The invention further relates to the method of producing titanium trichloride catalyst component and a method for polymerizing alpha-olefins such as propylene to highly stereoregular polyolefins in the presence of the titanium trichloride catalyst component and a cocatalyst such as an organoaluminum compound. More particularly, the invention relates to a highly active, highly crystalline shear resistant titanium trichloride which has been prepolymerized with a small amount of alpha-olefin.

2. Discussion of the Prior Art

Pretreatment of Ziegler-type catalysts with propylene is known in the art. The pretreatment is generally performed in order to stabilize the catalyst. For example, in British Pat. No. 1,300,734 (published Dec. 20, 1972) of Shell International Research Maatschappij N.V., it is taught that by contacting a Ziegler-type catalyst comprising a titanium halide and an organoaluminum compound with a small amount of an alpha-olefin a stabilized catalyst is obtained. By "stabilization", the patent teaches that reduction of catalytic activity during polymerization reaction does not occur such that the overall activity is maintained at a high level.

In accordance with British Pat. No. 1,384,603 of Shell International Research Maatschappij N.V., there is disclosed a titanium halide aluminum trialkyl polymerization catalyst which is stabilized against deteriorating during the polymerization reaction by prepolymerizing the catalyst at a temperature below 62° C. prior to its being employed in the conventional polymerization reaction.

In the British Pat. No. 1,408,611 (published Oct. 1, 1975) of Shell International Research Maatschappij N.V. there is disclosed the preparation of a titanium trichloride catalyst component which involves reducing titanium tetrachloride to a beta-type titanium trichloride, activating the titanium trichloride to a gamma titanium trichloride and thereafter contacting the same with propene in order to form a prepolymerized catalyst component.

In U.S. Pat. No. 3,404,096 of Lamborn, issued Oct. 1, 1968, there is disclosed a method of pretreating Ziegler-type catalysts with ethylene so as to form a curdy catalyst component which is useful for obtaining friable fine catalyst particles.

In U.S. Pat. No. 3,689,597 of Mahlman, issued Sept. 5, 1972, there is disclosed a method of obtaining fine polypropylene particles by polymerizing propylene in the presence of a titanium trichloride catalyst which has been pretreated with alpha-olefins.

Several methods describing the activation of titanium trichloride obtained by low temperature reduction of titanium tetrachloride with an organoaluminum compound are described in the published patent literature. The activation is generally accomplished by contacting the reduction product of titanium tetrachloride with complexing agents and with various halogenated compounds to obtain a purple titanium trichloride which is useful as a co-catalyst with an organo-metal compound for the polymerization of alpha-olefins.

More particularly, in Japanese Patent Application (OPI) No. 34478/1972, published on Nov. 21, 1972 and corresponding to British Pat. No. 1,391,068 there is described a process which comprises treating the reduced solids obtained by low temperature reduction of titanium tetrachloride with an organoaluminum compound with a complexing agent, e.g., an ether, and titanium tetrachloride.

In Japanese Patent Application (OPI) No. 112289/1975, published Sept. 3, 1975, there is described a process wherein the titanium trichloride-containing reduced solids product obtained from the low temperature reduction of titanium tetrachloride in the presence of an organoaluminum compound is treated with a complexing agent, e.g., ethers, and then the resulting brown TiCl₃ -containing catalyst is treated with carbon tetrachloride.

Additionally, in Japanese Patent Application (OPI) No. 143790/1975, published Nov. 19, 1975, a method is described comprising treating the reduced solids product with a mixture of a complexing agent and carbon tetrachloride.

In Japanese Patent Application (OPI) No. 149897/1976, published Dec. 23, 1976 and corresponding to British Pat. No. 1,484,086, there is described a process in which brown titanium trichloride obtained from the reduction of titanium tetrachloride in the presence of an organoaluminum halide and at low temperatures is subjected to heat treatment in the presence of a halogenated aliphatic or aromatic hydrocarbon in order to produce a violet titanium trichloride. It is further disclosed that the brown titanium trichloride obtained from the reduction step may be treated with a complexing agent, including ethers, prior to heat treatment.

In Japanese Patent Application (OPI) No. 227/1977, published Jan. 5, 1977, there is described a process which comprises heat-treating the reduced solid obtained from the low temperature reduction of titanium tetrachloride with an organoaluminum compound, treating the reduced solid with a complexing agent and then treating the resulting solids with an alkylaluminum dihalide or titanium tetrachloride.

Furthermore, in U.S. Pat. No. 3,825,524 there is described a process for the production of titanium trichloride catalyst having a high activity which includes contacting a crude titanium trichloride composition, obtained by reducing titanium tetrachloride with an organoaluminum chloride, with a mixed solvent system composed of (i) a main solvent of aliphatic or aromatic hydrocarbons, aromatic chlorinated hydrocarbons or trichloroethylene, and (ii) an auxilliary solvent, including ethers. The mixed solvent system is employed for the purpose of extracting undesirable components from the reduction product.

In co-pending U.S. Application Ser. Nos. 774,964, 774,946 and 774,947 there are disclosed processes for the production of titanium trichloride catalyst complexes useful for the polymerization of alpha-olefins in the presence of a co-catalyst such as an organo-metal compound. The process comprises reducing titanium tetrachloride with an organoaluminum halide compound at low temperature and thereafter treating at elevated temperatures the resulting reduced solid product with a chlorinated saturated hydrocarbon and in the further presence of a complexing agent such as an ether.

In Japanese Patent Application Publication No. Sho. 52-142691, of Chisso Corp., published Nov. 28, 1977, there is described a method of producing a titanium halide catalyst component wherein a small amount of propylene is present during the preparation of the titanium trichloride obtained during the reduction of titanium tetrachloride with an organoaluminum compound and therafter treating the obtained reduced solid with a Lewis acid and/or a complexing agent.

It is well known that during the formation of polyolefin particles obtained in the presence of transition metal halide catalysts, such as titanium halides, the polymer particles are essentially replicates of the catalyst particles. It is further known that during the activation of the titanium halides obtained from the low temperature reduction of titanium tetrachloride that the transition metal halide particles are friable, i.e., they will shear into smaller particles, i.e., fines. Therefore, it is highly desirable to obtain transition metal halide catalyst components which are essentially non-friable during activation and when subjected to mechanical shearing forces which may occur either during activation and polymerization.

SUMMARY OF THE INVENTION

In accordance with the present invention, a nonfriable, highly active Ziegler-type titanium chloride catalyst composition is obtained by reducing titanium tetrachloride to a titanium trichloride reduced solid product in the presence of an organoaluminum compound at a low temperature, e.g., in the range of about -50° C. to about 30° C., contacting the titanium trichloride reduced solid product with a minor amount of an alpha-olefin having at least three carbon atoms under polymerization conditions to obtain a titanium trichloride reduced solid product containing about 1 to about 1,000 wt% of prepolymerized alpha-olefin based on the weight of titanium trichloride thereby providing prepolymerized TiCl₃ reduced solid, and thereafter treating said prepolymerized titanium trichloride reduced solid product with one of (a) a chlorinated hydrocarbon having at least two carbon atoms and a Lewis base complexing agent or with (b) a Lewis acid such as TiCl₄ and a Lewis base complexing agent to convert said prepolymerized titanium trichloride reduced solid to a highly active, crystalline prepolymerized titanium trichloride composition. The process of prepolymerizing the titanium trichloride reduced solid product obtained from the low temperature reduction of titanium tetrachloride in the presence of an alkylaluminum compound results in titanium trichloride catalyst particles which are substantially resistant to fractionation, i.e., are non-friable, and therefore, can be readily converted to a purple form of titanium trichloride absent the production of "fines" by treatment of the prepolymerized titanium trichloride reduced solid with the halogenated hydrocarbon and Lewis base or by other methods of activation. The strengthening of the titanium trichloride reduced solid, therefore, allows for a wider range of activation conditions, as well as use of variety of solvents and activators which would normally disintegrate titanium trichloride particles. In other words, the prepolymerization of the titanium trichloride reduced solid product (the contacting of the reduced solid under polymerization conditions with a minor amount of an alpha-olefin) allows the reduction product to be activated under extreme conditions which heretofore would normally lead to catalyst attrition.

DETAILED DESCRIPTION OF THE INVENTION

The titanium trichloride-containing reduced solid used in the present invention is obtained by reducing titanium tetrachloride with an organoaluminum compound and preferably an alkylaluminum halide at low temperature (e.g., -50° C. to +30° C.) as described in patent application U.S. Ser. No. 774,964 which disclosure is hereby incorporated by reference. The alkylaluminum halide employed can be represented by the general formula R_(n) AlX_(3-n), wherein R represents an alkyl group having 1 to 18 carbon atoms, most preferably 2 to 6 carbon atoms, X represents a halogen atom, most preferably chloride, and n can be within the range of 0 to 3 and preferably 1 to 3, or a mixture or complex compound thereof. Illustrative of suitable alkylaluminum compounds are trialkylaluminums, dialkylaluminum halides, monoalkylaluminum dihalides and alkylaluminum sesquihalides, mixtures or complex compounds thereof. Examples of trialkylaluminums which can be employed are trimethylaluminum, triethylaluminum and tributylaluminum and the like. Examples of dialkylaluminum halides are dimethylaluminum chloride, diethylaluminum chloride, dibutylaluminum chloride, diethylaluminum bromide and diethylaluminum iodide and the like. Examples of the monoalkylaluminum dihalides are methylaluminum dichloride, ethylaluminum dichloride, butylaluminum dichloride, ethylaluminum dibromide and ethylaluminum diiodide and the like. Examples of the sesquihalides are ethylaluminum sesquichloride, propylaluminum sesquihalide and the like. Triethylaluminum, diethylaluminum chloride, ethylaluminum dichloride, ethylaluminum sesquichloride and mixtures thereof or complex compounds thereof, for example, a mixture of diethylaluminum chloride and ethylaluminum dichloride are particularly preferable.

The reduction step is carried out at a specified temperature which typically is between -50° C. and +30° C. by contacting titanium tetrachloride with the above-described organoaluminum compound. By way of example, to a solution of titanium tetrachloride in an inert solvent or diluent, e.g., a hydrocarbon having 5 to 12 carbon atoms such as n-pentane, isopentane, cyclopentane, n-hexane or isooctane, there is added dropwise a solution of alkylaluminum halide compound in said inert solvent or diluent. Conversely, a solution of titanium tetrachloride can be added dropwise to a solution of the alkylaluminum halide compound. Under carefully controlled conditions, the quantity of organoaluminum compound employed is generally about 0.5 to about 5 gram atoms as aluminum per 1 gram atom of titanium.

The specific temperatures and the amount of organoaluminum compound employed during the reduction step can be varied within the ranges disclosed herein, nevertheless associated with a specific organoaluminum compound there can be desirable concentrations and temperature ranges. In the case of diethylaluminum chloride, for example, (which will hereinafter be referred to as "DEAC") it is preferable to carry out the reduction at a temperature of about -50° C. to about +30° C., particularly about -5° C. to about +5° C., and to use DEAC in a proportion of about 0.5 to about 5 mols, particularly about 0.8 to about 1.5 mols, to 1 mol of titanium tetrachloride. For a mixture or complex of dialkylaluminum halide and alkylaluminum dihalide, for example, DEAC and ethylaluminum dichloride (which will hereinafter be referred to as "EADC"), it is preferable to carry out the reduction at at temperature of about -50° C. to about +30° C., particularly about -5° C. to about +5° C., and to use DEAC in a proportion of about 0.5 to about 4 mols, particularly about 0.8 to about 1.5 mols, and EADC in a proportion of about 0.01 to about 1.5 mols, particularly about 0.1 to about 1.2 mols, respectively based on 1 mol of titanium tetrachloride.

The period of time of reactant addition during the reduction step may vary greatly, depending upon the quantity of reactants used and the desirability of maintaining a specified reduction temperature. However, reactant addition, e.g., dropwise addition, is generally carried out for a period of time from about 30 minutes to about 3 hours.

Preferably, after reactant addition the reaction mixture is aged in order to complete the reduction reaction. Aging may be carried out by gradually elevating the temperature of the reaction mixture to a specified temperature within the range of about 20° C. to about 100° C. over a period of time of about 1 to 2 hours. Most preferably, aging is carried out by holding the reaction mixture, after reactant addition, at the reduction temperature for about one-half hour and then gradually elevating the temperature to about 65° for a period of time of about 1 hour and finally holding the reaction mixture at about 65° C. for about 1 hour. Caution should be taken during aging to prevent the titanium trichloride reduced solid from being subjected to conversion of the titanium trichloride-containing reduced solid to a more crystalline form. For example, by subjecting the titanium trichloride reduced solid to too high a temperature for a prolonged period of time during the aging step crystal conversion could occur.

The so obtained titanium trichloride reduced solid is an amorphous solid having a complicated composition comprising, as a main component, titanium trichloride and the alkylaluminum compound employed in the reduction, or a reaction product of titanium tetrachloride and the alkylaluminum halide compound. This composition varies depending upon the exact reducing methods and conditions. Where titanium tetrachloride is reduced with a mixture of DEAC and EADC, it comprises, as a main component, titanium trichloride and EADC and, in addition, aluminum compounds in various forms, the proportion of aluminum being about 0.2 gram atoms or more to 1 gram atom of titanium.

The so obtained reduced solid contains titanium trichloride of the beta-type and is brown to red-violet in color, depending upon specific reduction conditions employed.

The titanium trichloride reduced solid obtained as described above can be prepolymerized, i.e., contacted with a polymerizable alpha-olefin under polymerization conditions, directly without the addition of a reducing co-catalyst or it can be separated, washed in an inert solvent or diluent, if desirable, and then prepolymerized upon addition of a co-catalyst (aluminum alkyl) as it is or after drying in a conventional manner.

In accordance with this invention the alpha-olefins which can be employed in the prepolymerization step can have from 3 to 22 and desirably 3 to 8 carbon atoms. However, an alpha-olefin mixture having from 10 to 46 carbon atoms can also be employed. In accordance with a preferred embodiment of the invention, the alpha-olefins will contain no branching on the vinylic carbon atom. Illustrative of alpha-olefins which can be employed in accordance with this invention during the prepolymerization step are propylene, butene-1, pentene-1, hexene-1, heptene-1, 4-methyl-pentene-1 and the like. Preferably the alpha-olefin will contain from 3 to 6 carbon atoms and most preferably the alpha-olefin will be propylene.

The temperature of the reaction mixture during the alpha-olefin application can be from about 0° C. to 100° C. preferably 25° C. to about 60° C. and most preferably from about 30° C. to about 40° C. As in the aging step, prepolymerization conditions should be such as to prevent conversion of the reduced solid to a more crystalline form.

The alpha-olefin employed in accordance with the present invention for the prepolymerization of the titanium trichloride reduced solid can be added directly to the reaction product of the reduction step or it can be added to the washed reaction product in a suitable solvent. The amount of alpha-olefin employed can be in a mol ratio per total titanium halide reduced solid employed in a range of about 0.03 to 3000 times, and particularly at about 0.1 to 0.5 times. The mol ratios employed, therefore, will desirably provide a titanium halide prepolymerized with about 1 to 1,000 wt% of alpha-olefin based on the titanium halide and desirably from about 3 to about 100 wt.% and most preferably from about 6 to 30 wt.% of alpha-olefin based on the weight of titanium halide.

The time period over which the alpha-olefin can be allowed to react with the reduced solids is desirably in a range of about 1 minute to about 180 minutes, preferably in a range of 10 to about 120 minutes and most preferably about 30 minutes. The times will be function of the temperatures employed, the alpha-olefins employed as well as the degree of prepolymerization desired. Hence, the actual time employed would be determined by the artisan, the determination being well within the skill of the artisan.

Upon completion of prepolymerization the titanium trichloride reduced solid now prepolymerized with a minor amount of alpha-olefin is filtered and washed with an inert organic solvent so as to remove any reaction by-products.

In accordance with this invention, the prepolymerized titanium trichloride reduced solids obtained will manifest essentially no change in crystalline structure.

The prepolymerized reduced solid can be employed as a non-friable polymerization catalyst component.

The prepolymerized titanium trichloride reduced solid product can, in accordance with a preferred aspect, be activated to a highly active crystalline prepolymerized product in essentially two manners. One can employ a chlorinated hydrocarbon in combination with a Lewis base complexing agent or a Lewis acid in combination with a Lewis base complexing agent. In accordance with this invention it is preferable to employ the chlorinated hydrocarbon in combination with the Lewis base complexing agent.

As illustrative of the chlorinated hydrocarbons which can be employed in accordance with this invention are hexachloroethane, pentachloroethane, tetrachloroethane, trichloroethane, dichloroethane, monochloroethane, tetrachloroethylene, trichloroethylene, dichloroethylene, chloroethylene, octachloropropane, hectachloropropane, hexachloropropane, pentachloropropane, tetrachloropropane, trichloropropane, dichloropropane, monochloropropane, tetrachlorobutane, trichlorobutane, dichlorobutane, trichloropentane, dichloropentane, dichlorohexane, dichloroheptane, dichlorooctane, dichlorobenzene, trichlorobenzene, monochlorobenzene, dichloropropene, trichloropropene, and dichlorobutene.

A variety of chlorinated hydrocarbons can be employed during activation, e.g., the chlorinated products of aliphatic and aromatic hydrocarbons. The chlorinated products of the aliphatic saturated hydrocarbons are generally more effective. Desirably the chlorinated aliphatic hydrocarbons will have from about 2 to 8 carbon atoms and from about 2 to 6 chlorine atoms per molecule. The most preferred chlorinated hydrocarbons are the chlorinated ethanes. The effect of the chlorinated hydrocarbons appears to increase with the increased number of chlorine atoms per molecule desired. Desirably, therefore, the chlorinated hydrocarbons employed can be one of hexachloroethane, pentachloroethane, tetrachloroethane, trichloroethane. Most preferably the chlorinated hydrocarbon will be hexachloroethane.

The Lewis base complexing agent which can be employed in accordance with this invention will desirably contain at least one electron donating atom or group in the molecule and will preferably be one of an ether, ester, ketone, thioether, organophosphoric compound or organonitrogen compound or mixtures of these compounds. Most desirably the Lewis base complexing agent will be a dialkyl ether such as, for example, diethyl ether, diisopropyl ether, di-n-butyl ether, diisobutyl ether, diisoamyl ether, di-2-ethylhexyl ether, di-2-ethylheptyl ether, allyl ethyl ether, allyl butyl ether, diphenyl ether, anisole, phenetole, chloroanisole, bromoanisole, dimethyloxy benzene, and the like. Hence, the Lewis base complexing agent is an organic electron-donor compound containing phosphorous, sulfur, nitrogen and/or oxygen.

Useful examples of the thioethers are diethyl thioether, di-n-propyl thioether, dicyclohexyl thioether, diphenyl thioether, ditolyl thioether, ethylphenyl thioether, propylphenyl thioether, diallyl thioether, and the like. Useful examples of the organophosphorus compounds which can be employed in accordance with this invention are tri-n-butyl phosphine, triphenyl phosphine, triethyl phosphite, tributyl phosphite, and the like. Useful examples of the organonitrogen compounds are diethyl amine, triethyl amine, n-propyl amine, di-n-propyl amine, tri-n-propyl amine, aniline, dimethylaniline, and the like. As indicated above, the ethers are most preferably employed and above all are dialkyl ethers, preferably the alkyl groups containing from 4 to 8 carbon atoms. Most preferred are dialkyl ethers containing 4 or 5 carbon atoms. The ethers so employed can be symmetrical or asymmetrical ethers and hence the alkyl groups are selected from the group consisting of n-butyl, isobutyl, n-amyl, isoamyl, 2-methylbutyl and 2-ethylpropyl. Most preferably di-n-butyl ether and diisoamyl ether and n-butyl isoamyl ether are employed in accordance with this invention as a Lewis base complexing agent to be used in combination with the halogenated hydrocarbon.

In accordance with the present invention one may employ a Lewis acid in place of the halogenated hydrocarbon. However, the Lewis acid combination with a Lewis base is less desirable with respect to the results obtained than the halogenated hydrocarbon in combination with a Lewis base. The Lewis acids which can be used are selected from the halides of Group II or Group VII metals and halides of silica or boron. Illustrative of the Lewis acids which can be employed are, for example, MgCl₂, MnCl₄, AlCl₃, FeCl₃, TiCl₄, VCl₄, VCl₃, NiCl₂, CoCl₂, BCl₃, BF₃, SiCl₄. The preferred Lewis acid is TiCl₄.

The amout of Lewis acid employed in accordance with this invention can be from about 0.05 to about 50 times that of the weight of the prepolymerized titanium halide and preferably is from about 0.45 to about 15 times.

The proportion of Lewis base complexing agent employed is preferably between 0.1 and 2.5 mols, and especially between 0.5 and 1.8 mols, per mol of TiCl₃ present in the reduced solid. About 1 mol Lewis base per mol of TiCl₃ present in the reduced solid gives particularly good results.

In accordance with the present invention the activation step, i.e., the conversion of the prepolymerized reduced solid to a highly crystalline form of titanium trichloride is accomplished by contacting the prepolymerized reduced solid with either the chlorinated hydrocarbon and Lewis base complexing agent or the Lewis acid and Lewis base complexing agent. The contacting can be carried out by adding the prepolymerized reduced solid to an inert solvent or diluent, such as previously described so as to prepare a suspension and then adding, for example, the ether and hexachloroethane, thereto in order; by adding the ether to the prepolymerized reduced solid to prepare a suspension and then adding thereto hexachloroethane as a solution of hexachloroethane in the ether or an inert solvent; or by adding the prepolymerized reduced solid to a mixed solution of the ether and hexachloroethane or a mixed solution of ether, hexachloroethane and an inert solvent. The most convenient and favorable method consists in suspending the reduced solid in an inert solvent and then adding a mixture of ether, hexachloroethane and an inert solvent to the suspension.

In accordance with the present invention the chlorinated hydrocarbon such as hexachloroethane and the ether can be in a mol ratio to the titanium halide in the reduced solid of about at least 0.2 mol or more of chlorinated hydrocarbon preferably 0.1 mol to about 2.5 mols of ether and 0.5 to 1.5 mols of hexachloroethane. Greater or lesser ratios can be employed. However, the most desirable effects are obtained by employing the so stated specific mol ratios.

Moreover, the effects of the present invention are somewhat reduced if the prepolymerized reduced solid is contacted with the hexachloroethane or halogenated hydrocarbon prior to contacting the reduced solid with the ether. The treatment with ether and hexachloroethane appears together to provide a synergistic effect resulting in a catalyst having surprisingly excellent catalytic performances.

In accordance with the present invention the chlorinated hydrocarbon is employed in an amount of about 0.2 mols to about 3.0 mols per gram atom of titanium in the prepolymerized reduced solid and preferably the chlorinated hydrocarbons will be in the range of about 0.5 mols to about 1.5 mols particularly in the range of about 0.6 mols to about 1.2 mols per 1 gram atom of titanium in the prepolymerized reduced solid. Greater amounts of chlorinated hydrocarbon can be employed, however, no benefit is obtained therefrom. Lesser amounts of chlorinated hydrocarbon results in a less active catalyst.

The activation step is carried out at a temperature of about 50° to about 100° C. for a period of time of about 1 to 10 hours. Utilization of temperatures outside these ranges can be employed. However, activity of the catalyst appears to be best when the specified temperatures are employed. Most preferably, activation is carried out with the chlorinated hydrocarbon and ether at a temperature of about 80° C. to about 90° C. for about 3 to about 7 hours. Upon completion of the activation step the so obtained prepolymerized titanium trichloride catalyst composition is separated from the solvent, washed with an inert solvent or diluent and optionally dried in conventional manners. During the treatment step, the titanium halide of the reduced solid is converted whereby the so obtained titanium trichloride catalyst contains predominantly titanium trichloride of the delta-type, according to the classifications generally adopted (Journal of Polymer Science, 51, 1961, pp. 399-410). The so obtained titanium trichloride catalyst has a violet to purple color.

The titanium trichloride catalyst of the present invention is ordinarily employed as a catalyst for the polymerization of alpha-olefins by contacting the same with an organo-metal compound which is used as a cocatalyst for the Ziegler-type catalyst, for example, monoalkylaluminum dichloride, dialkylaluminum monochloride, alkyl aluminum sesquihalide or trialkylaluminum. One may also employ various compounds, for example, complexing agents such as ethers, amines or amides as well as phosphorous-containing compounds and nitrogen. The catalyst system for the polymerization of alpha-olefins employing the prepolymerized titanium trichloride catalyst of the present invention is exceedingly active for the homopolymerization or polymerization of alpha-olefins such as propylene, butene-1, 4-methylpentene-1, ethylene and the like and gives uniform polymer particles and a high degree of stereoregular polymers are used to polymerize propylene, for example, the catalytic activities are somewhat greater than about 2,200 grams of polymer formed per gram of titanium trichloride having at least 95% heptane insolubles content.

By so encapsulating the reduced solids particles in a polymer matrix the particles are strengthened to resist mechanical attrition, to resist particle breakup to fines when subjected to solvents and to resist particle break-up to fines during the activation step. Unexpectedly, the prepolymerization, performed in accordance with this invention does not, cause agglomeration of the catalyst particles but desirably allows the catalyst particles to retain their shape during activation and throughout any further polymerization reactions. These advantages are obtained even when the catalysts are employed in harsh solvents such as toluene.

The invention will be more clearly understood by reference to the following Examples. These Examples illustrate specific embodiments of the present invention and should not be construed to limit the invention in any way.

EXAMPLE 1--Preparation of the Titanium Halide Reduced Solid

This Example is illustrative of methods for preparing the reduced solids.

To a 2000 ml flask equipped with a stirrer and placed in a thermostat-controlled bath at 0° there was placed 700 ml of purified heptane and 250 ml of titanium tetrachloride. To the stirred mixture was added dropwise a mixture of 350 ml of diethylaluminum chloride, 117 ml of ethylaluminum dichloride and 400 ml of purified heptane. The reaction mixture was kept at 0° under constant stirring for a period of 3 hours and then aged for 2 hours at a temperature of 65° C.

The resulting titanium trichloride reduced solid in heptane solution was separated into 2 equal portions. With respect to one portion the titanium trichloride reduced solid was separated from the heptane supernatant and washed with purified heptane and dried at 65° for 30 minutes under reduced pressure. The second portion was neither washed nor separated from the heptane supernatant. A sample of the resulting reduced solid from both portion 1 and 2 were exmined by X-ray diffraction spectrum techniques. The spectrum essentially revealed that the reduced solid from an X-ray point of view essentially an amorphous solid which contained TiCl₃ of the beta-type.

EXAMPLE 2--Prepolymerization of the Washed Titanium Trichloride Reduced Solids

To a 250 ml glass bottle 18.5 cc of purified heptane there was added 10 gm of the dry TiCl₃ reduced solids obtained as described in Example 1 and sufficient EtAlCl₂ to provide one-half mol per mol of TiCl₃. The bottle was capped with a septum cap. The catalyst slurry was placed in a bath held at a temperature of 50° C. The bottle was purged with nitrogen and thereafter purged of nitrogen by purging with propylene for five minutes. During the purging with propylene the catalyst slurry layer was maintained in a quiescent position. After the propylene purge, propylene is passed through the stirred slurry maintained at a temperature of 25° C. for a time sufficient to provide 10 wt.% of polypropylene based on the weight of TiCl₃ present. Upon completion of prepolymerization the catalyst, i.e., prepolymerized reduced solid, was examined on an optical microscope and by X-ray diffraction techniques. The X-ray diffraction study revealed no change in the crystalline structure of the TiCl₃ reduced solid. The prepolymerized TiCl₃ reduced solid product was subjected to shearing forces by mechanically shearing the catalyst slurry on a microscope slide. It was observed that the catalyst was essentially non-friable.

Additional runs were made employing different co-catalyst and/or different reaction conditions. The prepolymerized reduced solid in each instance was non-friable.

The results of the prepolymerization runs are summarized in Table I.

                                      TABLE I                                      __________________________________________________________________________                      Prepolymerization Conditions                                          Mole Ratio                                                                              Catalyst    P   Prepolymerized Color                          Cocatalyst                                                                             Cocatalyst:TiCl.sub. 3                                                                  Concentration.sup.(1)                                                                  T °C.                                                                       (psig)                                                                             Color   Friability ±.sup.(2)               __________________________________________________________________________       EtAlCl.sub.2                                                                         0.5      0.54    50  1   red-violet                                                                             -                                       EtAlCl.sub.2                                                                         0.5      0.54    80  1   red-violet                                                                             -                                       EtAlCl.sub.2                                                                         0.5      0.54    25  1   red-violet                                                                             -                                       Et.sub.2 AlCl                                                                        0.5                                                                      EtAlCl.sub.2                                                                         0.5      0.54    50  1   red-violet                                                                             -                                       Et.sub.2 AlCl                                                                        0.5                                                                      Et.sub.2 AlCl                                                                        0.1      0.54    50  1   red-violet                                                                             -                                       Et.sub.2 AlCl                                                                        1.0      0.54    25  1   red-violet                                                                             -                                       Et.sub.3 Al                                                                          0.1      0.54    25  1   dark red-violet                                                                        -                                       Et.sub.3 Al                                                                          0.5      0.54    25  1   dark red-violet                                                                        -                                     __________________________________________________________________________      .sup.(1) gms/cc in heptane                                                     .sup.(2) + friable                                                             - nonfriable                                                             

EXAMPLE 3--Prepolymerization of the Slurred Titanium Trichloride Reduced Solid

To a 250 ml glass bottle was added 18.5 cc of reduced solid slurry prepared in Example 1 (second portion) containing 0.54 gm reduced solids per cc of slurry. Because the slurry obtained from the reduction step (Example 1) is employed there is no need to add a co-catalyst for the prepolymerization step. To the bottle was added a magnet and the bottle was capped with a septum cap. The bottle is inserted in a water bath maintained at a temperature of 25° C. The bottle is nitrogen purged and thereafter purged with propylene. Propylene was then passed through the constantly stirred slurry for a time sufficient to provide 10 wt.% of polypropylene based on the weight of TiCl₃ present. Upon completion of the prepolymerization the catalyst, i.e., prepolymerized reduced solids was examined on an optical microscope and by X-ray diffraction techniques. The X-ray diffraction study revealed no change in the crystalline structure of the TiCl₃ reduced solids and the solids when subjected to mechanical shearing such as with a glass slide did not fracture, i.e., was non-friable.

Additional runs (10-22) under varied conditions and/or alpha-olefins were made employing the reduced solids obtained from Example 1.

                                      TABLE II                                     __________________________________________________________________________     Prepolymerization Conditions                                                                             Wt. %                                                Catalyst      P   Olefin  Prepolymerized                                                                         Prepolymerized Color                         Concentration.sup.(1)                                                                    T °C.                                                                       (psig)                                                                             Prepolymerized                                                                         Olefin  Color   Friability ±.sup.(2)              __________________________________________________________________________      9.                                                                              0.54    25  1   Propylene                                                                              10      red-violet                                                                             -                                    10.                                                                              0.54    25  1   Propylene                                                                              10      red-violet                                                                             -                                      0.54    25  1   Propylene                                                                              10      red-violet                                                                             -                                      1.08    25  1   Propylene                                                                              10      red-violet                                                                             -                                      0.10    25  1   Propylene                                                                              10      red-violet                                                                             -                                      0.54    40  1   Propylene                                                                              10      red-violet                                                                             -                                      0.54    80  1   Propylene                                                                              10      red-violet                                                                             -                                      0.54    25  10  Propylene                                                                              10      red-violet                                                                             -                                      0.54    25  100 Propylene                                                                              10      red-violet                                                                             -                                      0.54    25  25  Propylene                                                                              10      red-violet                                                                             -                                      0.54    25  50  Propylene                                                                              10      red-violet                                                                             -                                    20.                                                                              0.54    50  1   Butene-1                                                                               10      red-violet                                                                             -                                      0.54    50  1   4-Methyl-                                                                              10      red-violet                                                                             -                                                      pentene-1                                                      0.54    50  1   Octene-1                                                                               10      red-violet                                                                             -                                      0.54    25  --  Propylene                                                                              10      red-violet                                                                             -                                                      Butene-1                                                       0.54    25  1   Propylene                                                                               3      dark red-violet                                                                        ±                                   0.54    25  1   Propylene                                                                               8      red-violet                                                                             -                                      0.54    25  1   Propylene                                                                              15      red-violet                                                                             -                                      0.54    25  1   Propylene                                                                              25      light red-                                                                             -                                                                      violet                                         0.54    25  1   Propylene                                                                              100     light red-                                                                             -                                                                      violet                                         0.54    25  1   Propylene                                                                              400     light red-                                                                             -                                                                      violet                                       __________________________________________________________________________      .sup.(1) gms/cc in heptane                                                     .sup.(2) + friable                                                             - nonfriable                                                             

EXAMPLE 4--Activation of the Prepolymerized TiCl₃ Reduced Solids

The following illustrates that the prepolymerized titanium trichloride reduced solids can be activated to a highly crystalline purple type titanium trichloride.

To a 250 ml glass bottle containing a stirring mechanism there was added 5 gm of prepolymerized reduced solid prepared in accordance with Example 3 (run 9). Thereafter 33.3 ml of a 1.75 molar hexachlorothane solution in heptane is added to the glass bottle. The mixture is shaken and heated to 60° C. To the heated mixture there is added 2.95 cc of 100% n-butyl ether. The slurry is heated to 80° C. and held at the temperature for 5 hours. At the conclusion of this treatment the prepolymerized TiCl₃ was purple in color. The slurry is cooled and the solid particles separated from the supernatent liquid. The solid was washed in 50 ml of boiling heptane and thereafter examined under a microscope and by electron microscopy. The prepolymerized TiCl₃ was now crystalline and was absent catalyst fines. The TiCl₃ was resistant to shear on a microscope slide.

EXAMPLE 5

A prepolymerized crystalline TiCl₃ was prepared in exactly the same manner as described in Example 3 with the exception that toluene was substituted for heptane. The obtained purple (red-violet product was examined under a microscope to determine its resistance to shearing. No evidence of shearing was found. No production of fines were evident although toluene was employed as the solvent.

EXAMPLE 6--Comparative Illustration

A reduced solid prepared as in Example 1 was examined under a microscope. This catalyst showed substantially no resistance to mechanical shearing forces in that the catalyst particles broke up into fines when subjected to pressure from a slide. The fines were screened out and the remaining reduced solids activated in the manner described in Example 4. An abundance of TiCl₃ fines were produced during this activation step.

EXAMPLE 7--Activation of Prepolymerized Titanium Halide Reduced Solids

To a 250 ml glass bottle there was added 5 gm of prepolymerized reduced solid as prepared in accordance with Example 3 (run 9). To the bottle was added 80 ml of heptane, 6.18 ml of 100% titanium tetrachloride and 4.22 ml of n-butyl ether. The reaction mixture was heated to 65° C. and held at that temperature for 2 hours. The catalyst turned purple in color. The catalyst particles are separated from the solvent and washed with boiling heptane. Upon examination under the microscope and X-ray diffraction the catalyst was noted to be crystalline and resistant to mechanical shearing forces.

EXAMPLE 8

The following runs illustrate that the prepolymerized activated TiCl₃ reduced solids catalyst component is an improved catalyst component as compared with activated TiCl₃ catalyst component which has not been prepolymerized in accordance with this invention.

100 mg (based on the weight of titanium trichloride) of the titanium trichloride catalyst component prepared according to Example 4 and diethylaluminum chloride in a proportion of 4 mols to 1 gm atom of titanium were charged into a 1000 ml autoclave. 600 ml of hydrogen and 800 ml of liquid propylene were introduced into the autoclave. The contents were heated to 68° C. and allowed to react for a period of 30 minutes. The unreacted propylene was removed and the separated polymer was washed. As a comparison, 100 mg of a reduced solid prepared in accordance with Example 1 and thereafter activated by treating with 33.3 ml of a 1.75 molar hexachloroethane solution in heptane and n-butyl ether as described in Example 4 was substituted for the prepolymerized activated TiCl₃ above. Propylene was polymerized under otherwise identical conditions.

As a further comparison a titanium trichloride prepared according to Example 5 was employed for the polymerization of propylene.

Results of this Example and the comparisons are summarized in Table III.

                                      TABLE III                                    __________________________________________________________________________                              Polymer Particles                                     Prepolymerization                                                                               Presence of                                                                            Cat. Eff.,                                                                          Heptane-Insol.                                   of TiCl.sub.3 Reduced Solid                                                                Solvent                                                                             Catalyst "fines"                                                                       W/W  %                                                __________________________________________________________________________     No          Heptane                                                                             Yes     147  95.6                                             Yes         Heptane                                                                             No      120  97.6                                             Yes         Toluene                                                                             No      120  >95                                              __________________________________________________________________________

EXAMPLE 9

The following Examples illustrate that the titanium trichloride reduced solid can be prepolymerized with monomers other than propylene. In accordance with this invention titanium trichloride reduced solid as prepared in Example 1 was prepolymerized with a monomer or mixture of monomers as listed in Table IV. The prepolymerized reduced solid was activated as described in Example 4.

Polypropylene was polymerized in the presence of the activated prepolymerized TiCl₃ catalyst in a manner as described in Example 8. The results are summarized in Table IV, where absence of catalyst dumping is a measure of the effectiveness of catalyst strengthening by monomer, i.e., absence of polymer fines.

                                      TABLE IV                                     __________________________________________________________________________                      mmols Monomer                                                                           gms Polymer                                          Example                                                                             Monomer mmols                                                                              mmol TiCl.sub.3                                                                         Mol TiCl.sub.3                                                                        Catalyst Clumping                             __________________________________________________________________________     A.   Propylene                                                                              48  20       8813   No                                            B.   Butene-1                                                                               53  20       9806   No                                            C.   Pentene-1                                                                              42  17.3     6769   No                                            D.   Hexene-1                                                                               50  20       9449   No                                            E.   Octene-1                                                                               51  20       8000   No                                            F.   (C.sub.22 -C.sub.46)--1.sup.a                                                          121 45.8     3752   No                                            G.   Isobutene                                                                              55  20       1872   Yes                                           H.   3-me-butene-1                                                                          51  20       2360   Partial                                       I.   4-me-pentene-1                                                                         50  20       4427   No                                            J.   Cis-butene-2                                                                           51  20       2360   Yes                                           K.   Cyclopentene                                                                           50  20       1183   Yes                                           L.   Butadiene-1,3                                                                          48  20       2233   Yes                                           M.   Acetylene                                                                              19.7                                                                               7.04      953   Yes                                           __________________________________________________________________________      .sup.a A mixture containing all alphaolefins within the indicated range. 

EXAMPLE 10

To a 0.1 gallon reactor are added 57.4 grams of TiCl₄ and 0.015 gallons of normal hexane. The stirred solution is cooled to 0° C. and 66.9 grams of DEAC solution (60 wt.% in normal hexane) is added over a five hour period. At the completion of DEAC addition, the stirred reaction mixture is held at 0° C. for 30 minutes, then warmed to 65° C. at 1° C. per minute and held at 65° C. for 1 hour. The stirred mixture is cooled to 35° C., and propylene is fed into the reaction mixture, at a rate of 0.31 grams per minute until 6.13 grams of propylene have been added. The reaction vessel is purged with nitrogen to remove all propylene from the solvent and vessel. The reaction mixture is washed by stirring with 0.6 gallons of hexane for 15 minutes, and by decanting hexane supernatant wash from settled catalyst slurry. The prepolymerized solids were examined.

To the prepolymerized reduced solid slurry there is added 0.003 gallons of hexane, and while stirring the slurry is heated to 60° C. Thereafter, a hot (55° C.) solution of 59 grams of hexachlorothane, 41.3 grams di-n-butyl ether and 0.16 gallons of normal hexane are added to the slurry over a period of 0.5 hours. The stirred reaction mixture is heated to 85° C. and held between 83° to 87° C. for five hours.

The reaction mixture is cooled to 65° C. and 0.07 gallons of hexane are added and the mixture stirred for 15 minutes. The hexane is decanted from settled catalyst slurry and the slurry is washed in hexane.

A comparison of the properties of the thus prepared catalysts components are given in Table V below.

                  TABLE V                                                          ______________________________________                                                                      Particle                                                                              Al:Ti:PP.sup.3                             Catalyst  Color     Friability                                                                              Diameter                                                                              Mole Ratio                                 ______________________________________                                         reduced solid                                                                            brown to  Yes      30     0.4:1:0                                              red-violet                                                           prepolymerized                                                                           pink to   No       32-35  0.4:1:0.3                                  reduced solid                                                                            red-violet                                                           Prepolymerized                                                                           purple    No       32-35  0.03:1:0.3                                 Activated Solid                                                                ______________________________________                                     

What is claimed is:
 1. In a process for the polymerization of α-olefins, wherein an α-olefin is contacted with a Ziegler-type catalyst comprising TiCl₃ and an organometallic compound under α-olefin polymerization conditions, the improvement comprising employing as said TiCl₃, a non-friable, highly active TiCl₃ catalyst composition produced by:(1) contacting TiCl₄ in an inert hydrogen diluent with an organoaluminum compound at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl₃ reduced solid product slurry, (2) contacting the reduced solid TiCl₃ slurry with a minor amount of an α-olefin having from 3 to 8 carbon atoms under polymerization conditions without addition of added cocatalyst so as to obtain a non-pulverized reduced TiCl₃ solid product containing about 1 to about 1,000 wt. % of prepolymerized α-olefin based on the weight of TiCl₃, and (3) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least two carbon atoms and a Lewis base complexing agent, or (b) TiCl₄ and a Lewis base complexing agent to convert the prepolymerized TiCl₃ reduced solid to a highly active, crystalline prepolymerized TiCl₃ composition.
 2. The process of claim 1 wherein said α-olefin employed in the prepolymerization step (2) contains no branching on the vinylic carbon atom.
 3. The process of claim 2 wherein said α-olefin employed in the prepolymerization step (2) is present in amounts so as to provided TiCl₃ prepolymerized with about 6 wt.% to 30 wt.% of said α-olefin based on the weight of TiCl₃.
 4. The process of claim 1 wherein said prepolymerized TiCl₃ solid product is treated with a chlorinated hydrocarbon and a Lewis base complexing agent.
 5. The process of claim 4 wherein the treatment is at a temperature in the range of about 50° C. to about 100° C. for about 1 to about 10 hours, the chlorinated hydrocarbon being present in an amount at least about 0.2 mol per gram atom of titanium and the Lewis base being present in an amount of at least 0.1 mol per mol of titanium.
 6. The process of claim 5 wherein the halogenated hydrocarbon is present in an amount of about 0.5 mol to about 1.5 mols per gram atom of titanium in the prepolymerized reduced solid and the Lewis base is present in a range of about 0.1 to about 2.5 mols per mol of titanium.
 7. The process of claim 1 wherein said prepolymerized TiCl₃ reduced solid product is treated with TiCl₄ and a Lewis base complexing agent.
 8. The process of claim 1 wherein the organometallic compound is a compound of a metal of Groups IA, IIA and B and IIIA of the Periodic Table and the organoaluminum compound employed in the reduction step (1) is an organoaluminum halide.
 9. The process of claim 8 wherein the organometallic compound is an organoaluminum halide.
 10. The process of claim 9 wherein said organoaluminum halide is of the general formula R_(n) AlX_(3-n) wherein R is an alkyl or aryl group having from 1 to 18 carbon atoms, X is a halogen and n is an integer of from 1 to
 3. 11. The process of claim 9 wherein the organoaluminum halide is a dialkyl aluminum chloride wherein said alkyl group can have from 2 to 6 carbon atoms.
 12. The process of claim 10 wherein the organoaluminum halide is a mixture of diethyl aluminum chloride and ethyl aluminum dichloride.
 13. The process of claim 1 wherein said organoaluminum compound employed in the reduction step (1) is present in a range of from about 1 to 5 gm atoms of aluminum to 1 gm atom of TiCl₄.
 14. The process of claim 4 or 7 wherein the Lewis base complexing agent is an organic-electron donor compound containing phosphorous, sulfur, nitrogen and/or oxygen.
 15. The process of claim 14 wherein said Lewis base complexing agent is selected from the group consisting of ethers, thioethers, thiols, organo phosphorous compounds, organo nitrogen compounds, ketones, esters and mixtures thereof.
 16. The process of claim 15 wherein said Lewis base complexing agent is a dialkyl ether.
 17. The process of claim 4 wherein said chlorinated hydrocarbon has from 2 to 8 carbon atoms and is selected from chlorinated saturated hydrocarbons, chlorinated unsaturated hydrocarbons or mixtures thereof.
 18. The process of claim 17 wherein said chlorinated hydrocarbon is selected from chlorinated aliphatic hydrocarbons, chlorinated alicyclic hydrocarbons, chlorinated aromatic hydrocarbons or mixtures thereof.
 19. The process of claim 18 wherein said chlorinated hydrocarbon is selected from hexachloroethane, pentachlorethane, tetrachloroethane, trichloroethane, dichloroethane, tetrachloroethane, hexachloropropane, pentachloropropane, tetrachloropropane, dichlorobutane and mixtures thereof.
 20. The process of claim 16 wherein said complexing agent is selected from the group consisting of di-n-butyl ether, di-n-amyl ether, diisoamyl ether, di-n-heptyl ether, di-2-ethyl hexyl ether, or mixtures thereof.
 21. The process of claim 19 wherein the chlorinated hydrocarbon is hexachloroethane.
 22. The process of claim 20 wherein said complexing agent is di-n-butyl ether.
 23. The process of claim 1 wherein said complexing agent is an ether.
 24. The process of claim 1 wherein said chlorinated hydrocarbon is hexachloroethane.
 25. The process of claim 1 wherein said α-olefin employed in the prepolymerization step (2) is present in an amount so as to provide TiCl₃ prepolymerized with about 3 to about 100 wt.% α-olefin based on the weight of TiCl₃.
 26. The process of claim 25 wherein said α-olefin employed in the prepolymerization step (2) is present in an amount so as to provide TiCl₃ prepolymerized with about 6 to 30 wt.% α-olefin based on the weight of TiCl₃.
 27. The process of claim 1 wherein said α-olefin employed in the prepolymerization step is propylene.
 28. In a process for the polymerization of propylene, wherein propylene is contacted with a Ziegler-type catalyst comprising TiCl₃ and an organometallic compound under propylene polymerization conditions, the improvement comprising employing as said TiCl₃, a non-friable, highly active TiCl₃ catalyst composition produced by:(1) contacting TiCl₄ in an inert hydrocarbon diluent with an organoaluminum compound at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl₃ reduced solid product slurry, (2) contacting the reduced solid TiCl₃ product slurry with a minor amount of an alpha-olefin having from 3 to 8 carbon atoms under polymerization conditions without addition of added co-catalysts so as to obtain a non-pulverized reduced TiCl₃ solid product containing from about 1 to about 1000 wt.% of prepolymerized alpha-olefin based upon the weight of TiCl₃, (3) treating said prepolymerized reduced solid with a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent to convert the prepolymerized TiCl₃ reduced solid to a highly active, crystalline, prepolymerized TiCl₃ composition.
 29. In a process for the polymerization of propylene, wherein propylene is contacted with a Ziegler-type catalyst comprising TiCl₃ and an organometallic compound under propylene polymerization conditions, the improvement comprising employing as said TiCl₃, a non-friable, highly-active TiCl₃ catalyst composition produced by:(1) contacting TiCl₄ in an inert hydrocarbon diluent with an organoaluminum halide at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl₃ solid product slurry, (2) contacting the reduced solid TiCl₃ product slurry with a minor amount of propylene under polymerization conditions without addition of added cocatalyst so as to obtain a non-pulverized reduced TiCl₃ solid product containing from about 1 to about 1,000 wt. % of prepolymerized propylene based upon the weight of TiCl₃, (3) treating said prepolymerized reduced solid with hexachloroethane and n-butyl ether to convert the prepolymerized TiCl₃ reduced solid to a highly active, crystalline, prepolymerized TiCl₃ composition. 